LNP™ LUBRICOMP™ LX91475 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xaoVeQ_LNPLUBRICOMPLX91475compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* LX91475 is a compound based on Polyetheretherketone resin containing proprietary fillers. Added features of this material include: High Temperature Bearing Grade, Internally lubricated. Also known as: LNP* LUBRICOMP* Compound LTW Product reorder name: LX91475 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 - 0.20 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.090 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11800 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 148 | MPa | ISO 527-2/5 |
| Fracture | 148 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 2.8 | % | ISO 527-2/5 |
| Fracture | 2.9 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 9700 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 210 | MPa | ISO 178 |
| -- 4 | 211 | MPa | ISO 178 |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.28 | ASTM D3702 Modified | |
| Flexural Strain at Break 5 | 3.3 | % | ISO 178 |
| Wear Factor - Washer | 10.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 6(23°C) | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7(23°C) | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8 | |||
| 0.45 MPa, unannealed, 64.0mm span | > 300 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | > 300 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 4.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 4.8E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.700 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 370 - 380 | °C | |
| Middle Temperature | 380 - 400 | °C | |
| Front Temperature | 380 - 400 | °C | |
| Mold Temperature | 175 - 190 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Break |
| 4 . | Yield |
| 5 . | 2 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP PP 40 GF NAT | RTP Company | PP, Unspecified | RTP |
| YUNGSOX® PP 1020L | Formosa Polypropylene | PP Homopolymer | YUNGSOX® PP |
| CERTENE™ LDF-0824B | Muehlstein | LDPE | CERTENE™ |
| DOW™ Electrical & Telecommunications HFDB-4201 EC | The Dow Chemical Company | LDPE | DOW™ Electrical & Telecommunications |
| Hostacom HKP 215D BLACK | LyondellBasell Industries | PP Homopolymer | Hostacom |