MAXAMID™ PA6G30UVHSL BK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Pier One Polymers, Inc. |
| Trademark: | MAXAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y5F95o_MAXAMID-PA6G30UVHSL-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MAXAMID™PA6 G30HSL is available in natural and custom colors, internal and external lubricants, UV stabilized and other modifications. Further information and details are available upon request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Ash Content | 27 to 33 | % | ASTM D4218 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 172 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 5.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 8620 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 221 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 207 | °C | ASTM D648 |
| Peak Melting Temperature | 215 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | < 0.20 | % | |
| Processing (Melt) Temp | 232 to 288 | °C | |
| Mold Temperature | 65.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2299 X 133087 A EG | RTP Company | PEEK | RTP |
| Promyde® B40 LN | NUREL, S.A. | Nylon 6 | Promyde® |
| KOPA® KN333NW | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| OmniCarb™ PC/PBT 1214 IM | OMNI Plastics, LLC | PC+PBT | OmniCarb™ |
| PharMed PharMed Tubing | Saint Gobain - Norton | TPE | PharMed |