OP - PC - Unfilled 46
| Category: | PC , Polycarbonate |
| Manufacturer: | Oxford Polymers |
| Trademark: | OP - PC - Unfilled |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xWgaQ1_OP---PC---Unfilled-46.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OP - PC - Unfilled 46 is a Polycarbonate (PC) material. It is available in North America for blow molding, extrusion, or injection molding. Primary attribute of OP - PC - Unfilled 46: Flame Rated. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2380 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 62.1 | MPa | |
| Break | 65.5 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 7.0 | % | |
| Break | 110 | % | |
| Flexural Modulus | 2340 | MPa | ASTM D790 |
| Flexural Strength | 93.1 | MPa | ASTM D790 |
| Compressive Strength | 86.2 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 800 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 138 | °C | |
| 1.8 MPa, Unannealed | 132 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 266 | °C | |
| Middle Temperature | 271 | °C | |
| Front Temperature | 277 | °C | |
| Nozzle Temperature | 277 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 288 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ HP0339W20L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Clariant Nylon 6 PA-211G13 | Clariant Corporation | Nylon 6 | Clariant Nylon 6 |
| Keyflex® BT 1068D | LG Chem Ltd. | TPC-ET | Keyflex® BT |
| Jampilen HP554P | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| IROSTIC® S 8735 | Huntsman Corporation | TPU, Unspecified | IROSTIC® |