| Category: | HDPE, MMW , High Density (MMW) Polyethylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xTLfot_Generic-HDPE-MMW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic HDPE, MMW This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.944 - 0.962 | g/cm³ | ASTM D792 |
| -- | 0.953 - 0.960 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.10 - 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| MD | 689 - 938 | MPa | ASTM D882 |
| TD | 703 - 1280 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 23.2 - 31.4 | MPa | ASTM D882 |
| TD : Yield | 24.4 - 30.3 | MPa | ASTM D882 |
| MD : Fracture | 51.7 - 54.8 | MPa | ASTM D882 |
| TD : Fracture | 17.9 - 24.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 590 - 870 | % | ASTM D882 |
| TD : Fracture | 10 - 980 | % | ASTM D882 |
| Dart Drop Impact (23°C) | 50 - 55 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 14 - 35 | g | ASTM D1922 |
| TD | 360 - 1200 | g | ASTM D1922 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 198 - 205 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic HDPE, MMWThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mowiol® 47-88 G2 | Kuraray Co., Ltd. | PVOH | Mowiol® |
| THERMOLAST® K TC5PCZ (Series: AD/PA/CS) | KRAIBURG TPE | TPE | THERMOLAST® K |
| XYRON™ X551V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Formolene® L62009X | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| ECP 121/1015 | TBA Electro Conductive Products Ltd. | EVA | ECP |