Torelina® A670X01
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Toray Resin Company |
| Trademark: | Torelina® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xPEee5_Torelina-A670X01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Torelina® A670X01 is a Polyphenylene Sulfide (PPS) product. It is available in Asia Pacific, Europe, or North America. |
| General Information | |
|---|---|
| Appearance |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 3.00 mm 1 | 2.3 | % | |
| Flow : 3.00 mm 2 | 2.3 | % | |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (23°C) | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 25 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 1800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 40 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 400 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 97.0 | °C | ISO 75-2/A |
| Melting Temperature | 278 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.2E-4 | cm/cm/°C | |
| Transverse | 1.2E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | 34 | kV/mm | IEC 60243-1 |
| Dielectric Constant 3(23°C, 1 MHz) | 3.00 | IEC 60250 | |
| Dissipation Factor 4(23°C, 1 MHz) | 2.0E-3 | IEC 60250 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bar Flow Length 5(320°C, 1.00 mm) | 180 | mm | Internal Method |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | 60% RH |
| 4 . | 60% RH |
| 5 . | 98 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 207.3H HS | RTP Company | Nylon 66 | RTP |
| WanBlend® WHT-890E5 | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | WanBlend® |
| ADENE NHQB | A.D. Compound spa | PP Homopolymer | ADENE |
| LITEN ZB 29 | UNIPETROL RPA | PE Copolymer | LITEN |
| LNP™ LUBRICOMP™ RFN17SXS compound | SABIC Innovative Plastics Europe | Nylon, Unspecified | LNP™ LUBRICOMP™ |