VESTAMID® D DX9322
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAMID® D |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xNPoSk_VESTAMID-D-DX9322.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Characterization: 15% ground-glass fiber reinforced, heat-stabilized Applications: low-warpage housings, coverings with sprayed-on elastomer seals Its advantages over PA 12 exhibit in the
The PA 612 compounds of the VESTAMID® D series consequently represent specialty products that complement the comprehensive selection of PA 12 compounds of the VESTAMID® L series. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.17 | 1.17 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 1.9 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 2.4 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.90 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3150 | 2650 | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | |||
| Yield | 63.0 | 53.0 | MPa | |
| Break | 59.0 | 47.0 | MPa | |
| Tensile Strain | ISO 527-2/1A | |||
| Yield | 8.0 | 12 | % | |
| Break | 18 | 23 | % |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C, Complete Break | 3.0 | 3.0 | kJ/m² | |
| 23°C, Complete Break | 4.0 | 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C, Complete Break | 43 | 48 | kJ/m² | |
| 23°C, Complete Break | 46 | 96 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 186 | 186 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 114 | 114 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 194 | 193 | °C | ISO 306/B |
| Melting Temperature 2 | 215 | 215 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 6.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.0E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+14 | -- | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 4.30 | -- | ||
| 1 MHz | 3.10 | -- | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.043 | -- | ||
| 1 MHz | 0.049 | -- | ||
| Comparative Tracking Index | IEC 60112 | |||
| Solution A 3 | 575 | -- | V | |
| Solution A 4 | > 600 | -- | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | HB | UL 94 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA612, MH, 14-030, GF15 | -- | ISO 1874 |
| Note Message | |
|---|---|
| 1 . | specimen 127x12.7x3.2 mm processing acc. to ISO 1874-2 |
| 2 . | 2nd Heating |
| 3 . | 100 drops Value |
| 4 . | 50 drops Value |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC 6926 NA 022 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Staramide RF007ESS | Eurostar Engineering Plastics | Nylon 66/6 | Staramide |
| XAREC™ C832 | Idemitsu Kosan Co., Ltd. | SPS | XAREC™ |
| Geon™ Vinyl Flexible XV3796 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Karina BLUE PVC COMPOUND 550-06/86-IS-SD (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |