ASTALOY™ PC/ABS M130E
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xEFAeh_ASTALOY-PC-ABS-M130E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALOY™ PC/ABS M130E is high impact alloy of Polycarbonate and ABS which is designed for extrusion applications requiring balance of impact toughness, heat resistance and processability. It is the sheet extrusion and thermoforming version of ASTALOY™ PC/ABS M130. Note: The letters "U" or "W" indicate additional UV stabilisation [ ie: ASTALOY™ PC/ABS M130EU ]. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 7.0 | g/10 min | |
| 250°C/3.8 kg | 4.0 | g/10 min | |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 51.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 150 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2350 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 81.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 650 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 60.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 98.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 103 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 110 | °C | |
| Vicat Softening Temperature | 132 | °C | ASTM D1525 5 |
| CLTE - Flow | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695.2.12 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Screen Mesh - Screen Pack 6 | 20.0 to 40.0 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Screw Cooling | Optional | ||
| Drying Temperature | 95.0 to 100 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Cylinder Zone 1 Temp. | 190 to 210 | °C | |
| Cylinder Zone 2 Temp. | 200 to 220 | °C | |
| Cylinder Zone 3 Temp. | 210 to 230 | °C | |
| Cylinder Zone 4 Temp. | 220 to 240 | °C | |
| Cylinder Zone 5 Temp. | 230 to 250 | °C | |
| Melt Temperature | 220 to 250 | °C | |
| Die Temperature | 220 to 250 | °C | |
| Take-Off Roll | 100 to 125 | °C | |
| Back Pressure | 10.0 to 25.0 | MPa |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| 6 . | Front to Rear |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRAMID® 4210G15 | Samyang Corporation | Nylon, Unspecified | TRAMID® |
| Comai 735-1 AB | Comai Ltda | LLDPE | Comai |
| EVALENE® HDPE HP17411 | JG Summit Petrochemical Corporation | HDPE | EVALENE® HDPE |
| Flexirene® FH 56 A | Versalis S.p.A. | LLDPE | Flexirene® |
| Hostacom BB 136 G | LyondellBasell Industries | PP Impact Copolymer | Hostacom |