POLYFORT® FPP 8842U
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | A. Schulman Inc. |
| Trademark: | POLYFORT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bwfoOE_POLYFORT-FPP-8842U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP 20% Talc |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow 1 | 0.85 to 0.90 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 21.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 65 | % | ASTM D638 |
| Flexural Modulus 4 | 1780 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 100 | °C | |
| 1.8 MPa, Unannealed | 53.0 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 21 | % | ASTM D5630 |
| Note Message | |
|---|---|
| 1 . | 5x7 in plaque |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prixene® EL010E20 | POLYMAT | LLDPE | Prixene® |
| TRIREX® Compound 3025PE | Samyang Corporation | PC | TRIREX® Compound |
| Ultramid® A3EG3 | BASF Corporation | Nylon 66 | Ultramid® |
| INEOS LDPE 22H760 | INEOS Olefins & Polymers Europe | LDPE | INEOS LDPE |
| LONGLITE® PBT 3020-200X | CCP Group | PBT | LONGLITE® PBT |