Prisma® 1410
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Braskem |
| Trademark: | Prisma® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xEE1HD_Prisma1410.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Prisma 1410 is a high melt flow rate random copolymer, designed for injection moulding. This product exhibits exceptional transparency, very good stiffness/impact strength balance and excellent processability. Applications: High-transparency parts and packages. This product has excellent processability, high productivity, excellent balance stiffness / impact. Processing: Injection Moulding |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.902 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 40 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R grade, injection molding | 79 | ASTM D785 | |
| R scale 1 | 80 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, injection molding | 29.0 | MPa | ASTM D638 |
| Yield, injection molding | 28.0 | MPa | ISO 527-2 |
| Tensile Elongation (Yield, Injection Molded) | 14 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus - 1% Secant | |||
| Injection Molding | 1000 | MPa | ASTM D790 |
| Injection Molding | 1050 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -20°C, injection molding | 15 | J/m | ASTM D256 |
| 23°C, injection molding | 50 | J/m | ASTM D256 |
| -20°C, injection molding | 1.3 | kJ/m² | ISO 180 |
| 23°C, injection molding | 2.8 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, injection molded | 81.0 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 82.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, injection molded | 50.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 129 | °C | ISO 306/A, ASTM D1525 2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | |||
| 1000 µm, injection molding | 8.0 | % | ASTM D1003 |
| 1000 µm, injection molding | 8.0 | % | ISO 13468-1 |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PE 6752E (516H5) | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| NOVAPOL® LF-Y819 Series | NOVA Chemicals | LDPE | NOVAPOL® |
| Lifoflex® UV FLAM 30600 | Müller Kunststoffe GmbH | SEBS | Lifoflex® |
| LNP鈩?STAT-KON鈩?Noryl_HMC1010 compound | SABIC Innovative Plastics | PPE+PS | LNP™ STAT-KON™ |
| LNP™ LUBRICOMP™ DFP32 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |