Sumikon® PM-9640
| Category: | Phenolic , Phenolic |
| Manufacturer: | Sumitomo Bakelite Co., Ltd. |
| Trademark: | Sumikon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MtTmxx_Sumikon-PM-9640.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sumikon®PM-9640 is a phenolic (Phenolic) product,. It can be processed by injection molding and is available in North America or Asia Pacific. Sumikon®PM-9640 applications include electrical/electronic applications, wire and cable, housing and automotive industries. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.77 | g/cm³ | ASTM D792 |
| -- | 1.78 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.40 | % | ASTM D955 |
| -- | 0.30 - 0.50 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr | 0.070 | % | ASTM D570 |
| 23°C, 24 hr | 0.050 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 20000 | MPa | ASTM D638 |
| Tensile Strength | 95.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.50 | % | ASTM D638 |
| Flexural Modulus (23°C) | 17000 | MPa | ASTM D790 |
| Flexural Strength | |||
| 23°C | 200 | MPa | ASTM D790 |
| -- | 230 | MPa | ISO 178 |
| Compressive Stress | 275 - 315 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.4 | kJ/m² | ISO 179 |
| Notched Izod Impact | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 220 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 210 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | |||
| Flow | 2.3E-5 | cm/cm/°C | ASTM D696 |
| Flow | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength | |||
| -- | 13 | kV/mm | ASTM D149 |
| -- | 15 | kV/mm | IEC 60243-1 |
| Arc Resistance | 136 | sec | ASTM D495 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| Insulation Resistance, JIS K 6911, as molded: 1E11 to 1E13Insulation Resistance, JIS K 6911, after boiling: 1E10 to 1E12Arc Resistance, JIS K6911: 125 secAppearance after healing, JIS K6911, @ 2 hrs: 200°CAll ISO values were tested in accordance with JIS specifications. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx TPP2B30 | The Matrixx Group, Inc. | PP Copolymer | Matrixx |
| Salflex 623TIM | Salflex Polymers Ltd. | PP Copolymer | Salflex |
| TITANPRO® SM398 | Lotte Chemical Titan (M) Sdn. Bhd. | PP Random Copolymer | TITANPRO® |
| Vital-Line SHE5240B | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| DENIFORM 0037-M | Vamp Tech | Acetal (POM) Copolymer | DENIFORM |