Surlyn® 8660
| Category: | EMAA , Ethylene Methacrylic Acid |
| Manufacturer: | DuPont Packaging & Industrial Polymers |
| Trademark: | Surlyn® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | woeyiw_Surlyn-8660.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Surlyn® 8660 is a sodium ionomer thermoplastic resin. It is available for use in conventional extrusion and injection equipment, to create various sheets or shapes. Surlyn® 8660 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.950 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Ion Type | Sodium |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Resistance - NBS Index | 170 | ASTM D1630 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Freezing Point | |||
| -- | 74 | °C | ASTM D3418 |
| -- | 74 | °C | ISO 3146 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 62 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C, Compression Molded 1 | 13.0 | MPa | ASTM D638 |
| Break, 23°C | 23.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 470 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | ASTM D790 | ||
| -20°C | 646 | MPa | |
| 23°C | 230 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 5.9 | J/m | ASTM D256 |
| Tensile Impact Strength | ASTM D1822 | ||
| -40°C | 270 | kJ/m² | |
| 23°C | 345 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 71.0 | °C | ASTM D1525, ISO 306 |
| Peak Melting Temperature | 95.0 | °C | ASTM D3418, ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (6350 µm) | 11 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 185 to 285 | °C |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Riteflex® 672 | Celanese Corporation | TPC-ET | Riteflex® |
| Nypol® PA A3 G35 HS UV RH PRTA010 NR346 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Di-Pak™ E-4595-3 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| FHR Polypropylene AP5206-HN | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| I. Stern WC-103 | I. STERN & CO. INC. | PS (GPPS) | I. Stern |