SABIC® STAMAX 40YM243 resin
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | SABIC® STAMAX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wccoQq_SABIC-STAMAX-40YM243-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® STAMAX 40YM243 is a 40% long glass fiber reinforced UV stabilized polypropylene. The glass fibers are chemically coupled to the PP matrix, resulting in high stiffness and strength. The IMDS is 209768490. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.21 | g/cm³ | ASTM D792 |
| -- | 1.22 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8470 | MPa | ASTM D638 |
| -- | 8300 | MPa | ISO 527-2/1 |
| 80°C | 5700 | MPa | ISO 527-2/1 |
| 120°C | 4500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 108 | MPa | ASTM D638 |
| Fracture | 121 | MPa | ISO 527-2/1A/50 |
| Fracture, 80°C | 75.0 | MPa | ISO 527-2/1A/50 |
| Fracture, 120°C | 54.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Fracture 3 | 1.8 | % | ASTM D638 |
| Fracture | 2.1 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 4 | 7680 | MPa | ASTM D790 |
| 64.0mm span 5 | 7850 | MPa | ISO 178 |
| 80°C, 64.0mm span 6 | 5550 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 7 | 28 | kJ/m² | ISO 179/1eA |
| 23°C 8 | 22 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 9 | ISO 179/1eU | ||
| -30°C | 48 | kJ/m² | ISO 179/1eU |
| 23°C | 68 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact 10(23°C) | 18 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact 11(23°C, Energy at Peak Load) | 8.10 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 158 | °C | ASTM D648 |
| 1.8 MPa, not annealed 12 | 157 | °C | ISO 75-2/A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Fiber Content | 40 | % | ISO 3451 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 230 - 290 | °C | |
| Middle Temperature | 225 - 285 | °C | |
| Front Temperature | 220 - 280 | °C | |
| Nozzle Temperature | 220 - 280 | °C | |
| Processing (Melt) Temp | 220 - 280 | °C | |
| Mold Temperature | 20.0 - 80.0 | °C | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Screw Speed: Lowest Possible |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 80*10*4mm, Cut |
| 8 . | 80*10*4 mm, Cut |
| 9 . | 80*10*4mm, Cut |
| 10 . | 80*10*4mm, Cut |
| 11 . | 6.60 m/sec |
| 12 . | 80*10*4mm, Cut |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SE801G30 | RJM International, Inc. | AS | RJM |
| Stylac™ VA518 | Asahi Kasei Chemicals Corporation | ABS | Stylac™ |
| ColorRx® PP1-0500RX | LTL Color Compounders, Inc. | PP Homopolymer | ColorRx® |
| KumhoSunny PA/ABS HNB0225 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS+Nylon | KumhoSunny PA/ABS |
| Leona™ 1300G | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |