POLYAXIS® LP 8000
| Category: | mHDPE , Metallocene High Density Polyethylene |
| Manufacturer: | A. Schulman Inc. |
| Trademark: | POLYAXIS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wWweTk_POLYAXISLP8000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PolyAxis LP-8000 is a high density polyethylene intended for the rotational molding industry. This stiff yet tough compound has been used in watercraft with good success. |
| General Information | |
|---|---|
| Additive |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 0.945 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.6 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield, Rotational Molded) | 22.1 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Rotational Molded) | 500 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Rotational Molded) | 1000 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength (-40°C, 3.18 mm, Rotational Molded) | 88 | J | ARM |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Formolene® 3312B | Formosa Plastics Corporation, U.S.A. | PP Random Copolymer | Formolene® |
| Karina IVORY PVC COMPOUND TR-781-35/1-B-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PLUSTEK PB202G50BK39 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |
| Pro-fax PL395N | INDELPRO, S.A. de C.V. | PP Homopolymer | Pro-fax |
| NHU-PPA N201 | Zhejiang NHU Comp. Ltd. | PPA | NHU-PPA |