Rilsamid® AMN Noir P20 TLD
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Arkema |
| Trademark: | Rilsamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DxC5cI_Rilsamid-AMN-Noir-P20-TLD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsamid ® AMN Noir P20 TLD is a black coloured polyamide 12. This grade is plasticized and designed for injection molding. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Additive |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (235°C/2.16 kg) | 44.0 | cm³/10min | ISO 11357 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 30°C, 24 hr, 2.00 mm | 1.2 | % | |
| Flow : 30°C, 24 hr, 2.00 mm | 1.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 550 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 31.0 | MPa | |
| Break | 50.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 19 | % | |
| Break | > 200 | % | |
| Flexural Modulus | 530 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 174 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA12-P, MHLR, 12-005 | ISO 1874 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Yuyao PBT 3066G30 | Yuyao Tenglong Plastics Co., Ltd. | PBT | Yuyao PBT |
| Aurora PVC AP2130 Series | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |
| Karina CLEAR PVC COMPOUND 60/231-DA-AT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OxyVinyls® 240F | OxyVinyls, LP | PVC Homopolymer | OxyVinyls® |
| CERTENE™ PHM-20AN | Muehlstein | PP Homopolymer | CERTENE™ |