SCHULAMID® 66 GF 15 HI H
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w8Shh5_SCHULAMID-66-GF-15-HI-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% glass fibre reinforced and impact modified polyamid 66-compound, heat stabilized. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.20 | -- | g/cm³ | ISO 1183/A |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5400 | 3200 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 95.0 | 65.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.8 | 15 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 4500 | -- | MPa | ISO 178 |
| Flexural Stress 2(5.0% Strain) | 150 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | -- | kJ/m² | |
| 23°C | 10 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 35 | -- | kJ/m² | |
| 23°C | 55 | 80 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | > 250 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 238 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | > 250 | -- | °C | ISO 306/A50 |
| -- | 232 | -- | °C | ISO 306/B50 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | 350 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (2.00 mm) | 30 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | 700 | -- | °C | |
| 3.00 mm | 700 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.50 mm | 725 | -- | °C | |
| 3.00 mm | 725 | -- | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx FPP5A20CC | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| Rainmaker Polypropylene MCHPGL20 | Rainmaker Polymers LLC | PP Homopolymer | Rainmaker Polypropylene |
| Moplen EP 400H | LyondellBasell Industries | PP Copolymer | Moplen |
| Hanwha Total PE R901P | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | HDPE | Hanwha Total PE |
| Huafon JF-HSY-9580 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |