Diamond ABS 4012B
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Diamond ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vy5Upu_Diamond-ABS-4012B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Diamond ABS 4012B is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by blow molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792, ISO 1183/A |
| Melt Mass-Flow Rate (MFR) 1 | |||
| 220°C/10.0 kg | 1.3 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 2.1 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.40 to 0.60 | % | ASTM D955 |
| Across Flow | 0.97 | % | ISO 294-4 |
| Flow | 1.1 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 959 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 39.0 | MPa | ASTM D638 |
| Yield | 40.0 | MPa | ISO 527-2/50 |
| Break | 32.0 | MPa | ISO 527-2/50 |
| Flexural Modulus | |||
| Tangent 3 | 1870 | MPa | ASTM D790 |
| -- 4 | 1900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 340 | J/m | ASTM D256 |
| 23°C | 32 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C | 25.0 | J | |
| 23°C | 27.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 84.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.18 mm | 84.4 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 101 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 115 | °C | ASTM D1525 5 |
| CLTE | ASTM E831 | ||
| Flow | 8.8E-5 | cm/cm/°C | |
| Transverse | 1.1E-4 | cm/cm/°C |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 97 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 190 to 250 | °C | |
| Middle Temperature | 190 to 250 | °C | |
| Front Temperature | 190 to 250 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | 51 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ryton® QC160N | Solvay Specialty Polymers | PPS | Ryton® |
| tefabloc® TO 132 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| ADENE NTFA | A.D. Compound spa | PP Homopolymer | ADENE |
| Kynar® 5301 | Arkema | Plastics Additive, Other | Kynar® |
| ISOTHANE® 1095A | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |