Trexprene® A55BW
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | Trexprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v7Zd8D_Trexprene-A55BW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Product Description: TREXPRENE ® A55BW is a heat and UV stabilized PP/EPDM based Thermoplastic Vulcanized Elastomer (TPV) and is primarily intended for Exterior applications. This material can be processed using Extrusion, Injection, or Blow Molding equipment. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 to 0.990 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 15 sec) | 52 to 60 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Across Flow 1(100% Strain) | 1.80 | MPa | ISO 37 |
| Tensile Stress - Across Flow 2(Yield) | 5.50 | MPa | ISO 37 |
| Tensile Elongation - Across Flow 3(Break) | 590 | % | ISO 37 |
| Tear Strength - Across Flow 4 | 27 | kN/m | ISO 34-1 |
| Compression Set | |||
| 125°C, 70 hr | 39 | % | ASTM D395B |
| 125°C, 70 hr 5 | 39 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (135°C, 1000 hr) | 5.7 | % | ISO 188 |
| Change in Tensile Strain at Break in Air (135°C, 1000 hr) | -0.90 | % | ISO 188 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | |||
| -- | -56.0 | °C | ASTM D746 |
| Type B | -56.0 | °C | ISO 812 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Accelerated Weathering Duration 6 | Delta E < 3 | SAE J2527 | |
| Ozone Resistance (40°C) 7 | 0 Rating | ISO 1431-1 | |
| Weatherability 8 | SAE J1976 | ||
| Arizona | Delta E < 3 | ||
| Florida | Delta E < 3 |
| Note Message | |
|---|---|
| 1 . | Type 1, 500 mm/min |
| 2 . | Type 1, 500 mm/min |
| 3 . | Type 1, 500 mm/min |
| 4 . | Method Ba, Angle (Unnicked), 500 mm/min |
| 5 . | Type A |
| 6 . | Extended UV Filters, 2500 kJ/m 2 |
| 7 . | 100 pphm, Method A |
| 8 . | 2 years exposure, Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Caltex PP M560W | GS Caltex | PP Impact Copolymer | Caltex PP |
| APICAL 120AF616 | Kaneka Corporation | PI, TS | APICAL |
| Cheng Yu ML848 | Cheng Yu Plastic Company Limited | PC | Cheng Yu |
| Daelim Po1y® EP2001EN | DAELIM INDUSTRIAL CO., LTD. | mLLDPE | Daelim Po1y® |
| LNP™ THERMOCOMP™ EC006 compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |