Ultrathene® UE672102
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Ultrathene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vxeMnw_Ultrathene-UE672102.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ULTRATHENE UE672 is an EVA copolymer with excellent impact strength, heat sealability, good toughness and flexibility. Applications may include flexible packaging films for food and healthcare, as well as liquid and heavy duty packaging and pallet stretch film. UE672 contains antioxidant and high levels of slip and antiblock additives. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 13.5 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 90.3 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 91.0 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 6.62 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 5.52 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 30.5 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 29.8 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 18 | % | ASTM D882 |
| TD : Yield, 38 µm, blown film | 16 | % | ASTM D882 |
| MD : Broken, 38 µm, blown film | 300 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 600 | % | ASTM D882 |
| Dart Drop Impact (38 µm, Blown Film) | 570 | g | ASTM D4272 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 92 | g | ASTM D1922 |
| TD : 38 µm, blown film | 130 | g | ASTM D1922 |
| Oxygen Transmission Rate (23°C, 38 µm, blown film) | 8900 | cm³/m²/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (38°C, 38 µm, blown film) | 85 | g/m²/24 hr | ASTM F372 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 80.0 | °C | ASTM D1525 |
| Melting Temperature | 94.4 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.1 µm, Blown Film) | 88 | ASTM D2457 | |
| Haze (38.1 µm, Blown Film) | 1.5 | % | ASTM D1003 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| NAS 1(38.1 µm) | 78.0 | ASTM D1746 | |
| Physical properties measured on 1.5 mil film produced on a 2" BGE extruder w/4" Davis-Standard die, 25 mil die gap, 420 °F melt temperature @50 lb/hr, 2:1 BUR. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 232 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ASTALON™ S2000UR | Marplex Australia Pty. Ltd. | PC | ASTALON™ |
| CP PRYME® Nylon 66 NN100STL NAT | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |
| DOWLEX™ 2606 GC | The Dow Chemical Company | LLDPE | DOWLEX™ |
| LUVOCOM® 1/CF/40 | LEHVOSS Group | Nylon 66 | LUVOCOM® |
| Rotuba CAB B9024 (16% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |