Repol H050MN is recommended for Injection Moulding and is an ideal choice as a compounding base and blending material in furniture compound. It is also suitable for moulding rigid containers, housewares and thermowares. Repol H050MN contains nucleating agent for high rigidity, reduced cycle time and antistatic agent that reduces static charge build-up in products. |
General Information | |
---|---|
Additive |
|
Features |
|
Uses |
|
Agency Ratings |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.4 | g/10 min | ASTM D1238 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength 1(Yield, Injection Molded) | 36.0 | MPa | ASTM D638 |
Tensile Elongation 2(Yield, Injection Molded) | 10 | % | ASTM D638 |
Flexural Modulus - 1% Secant (Injection Molded) | 1750 | MPa | ASTM D790A |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (23°C, Injection Molded) | 35 | J/m | ASTM D256 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (0.45 MPa, Unannealed) | 110 | °C | ASTM D648 |
Note Message | |
---|---|
1 . | Type I, 50 mm/min |
2 . | Type I, 50 mm/min |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Miramid® SE50CW | BASF Leuna GmbH | Nylon 66 | Miramid® |
TECHNO ABS 150 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
C-Clear™ K8272 | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | C-Clear™ |
Lion Idemitsu Composites PPS C-7075SG | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
POLYblend PC/ABS 65 M10 | Polykemi AB | PC+ABS | POLYblend |