GLAMIDE® NB-1700
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vkwnEV_GLAMIDE-NB-1700.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GLAMIDE®NB-1700 is a polyamide product,. It is available in North America. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.06 | -- | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 28 | -- | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.70 - 1.0 | -- | % | ASTM D955 |
| 3.00 mm | 1.4 - 1.8 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 24 hr | 1.1 | -- | % | ASTM D570 |
| Equilibrium, 65% RH | 2.4 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 95.0 | 90.0 | MPa | ASTM D638 |
| Yield, 23°C | 55.0 | 34.0 | MPa | ASTM D638 |
| Yield, 80°C | 14.0 | 11.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 100 | 200 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 3500 | 3100 | MPa | ASTM D790 |
| 23°C | 2200 | 900 | MPa | ASTM D790 |
| 80°C | 700 | 300 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 130 | 125 | MPa | ASTM D790 |
| Yield, 23°C | 77.0 | 48.0 | MPa | ASTM D790 |
| Yield, 80°C | 19.0 | 15.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 40 | 60 | J/m | ASTM D256 |
| 23°C | 110 | 450 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 145 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 61.0 | -- | °C | ASTM D648 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 18 | 14 | kV/mm | ASTM D149 |
| Arc Resistance | 125 | 110 | sec | ASTM D495 |
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Melt Flow Rate, ASTM D1238: 25 to 30 g/10 minTensile Elongation, ASTM D638, 23°C: >100 %Comparative Tracking Index, IEC Method: >600 V |
| 调节后的 Tensile Elongation, ASTM D638, 23°C: >200 %Comparative Tracking Index, IEC Method: >600 V |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 245 - 285 | °C | |
| Mold Temperature | 30.0 - 80.0 | °C | |
| Injection Pressure | 30.0 - 60.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® MR409 22H-GY1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Ultramid® A3X3G5 | BASF Corporation | Nylon 66 | Ultramid® |
| Dryflex® 602350S | ELASTO | SEBS | Dryflex® |
| Polene LDPE J 4324 | TPI Polene Public Company Limited | LDPE | Polene LDPE |
| GELOY™ INP984 resin | SABIC Innovative Plastics | ASA | GELOY™ |