LNP™ LUBRICOMP™ KL004A compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Homopolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vZSdoG_LNPLUBRICOMPKL004Acompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP LUBRICOMP KL004A is a compound based on Acetal Homopolymer resin containing PTFE. Added features of this material include:internal lubricated. This grade was previously known as LNP Fulton* 404 D. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 2.0 - 2.2 | % | ASTM D955 |
| Transverse flow : 24 hours | 2.0 - 2.2 | % | ASTM D955 |
| Water Absorption (24 hr, 50% RH) | 0.23 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2550 | MPa | ASTM D638 |
| -- | 2700 | MPa | ISO 527-2/1 |
| Tensile Strength 2(Break) | 56.1 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture 3 | 11 | % | ASTM D638 |
| Fracture | 9.4 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 2620 | MPa | ASTM D790 |
| -- 5 | 2900 | MPa | ISO 178 |
| Flexural Strength 6(Yield, 50.0 mm Span) | 86.0 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.23 | ASTM D3702 Modified | |
| With Self-Static | 0.090 | ASTM D3702 Modified | |
| Wear Factor - Washer | 12.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 590 | J/m | ASTM D256 |
| 23°C 7 | 4.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D4812 |
| 23°C 8 | 39 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 95.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 9 | 98.0 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax PD702NW | LyondellBasell Industries | PP Homopolymer | Pro-fax |
| Vinnolit® K 704 | Vinnolit GmbH & Co. KG | PVC Alloy | Vinnolit® |
| Durez® 23570 (Compression) | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| Complet® LCF25-LGF25-PA66 | PlastiComp, Inc. | Nylon 66 | Complet® |
| CP PRYME® Polystyrene PS100-14M | Chase Plastics Services Inc. | PS (GPPS) | CP PRYME® Polystyrene |