LNP™ STAT-KON™ DX02437 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rbWT2l_LNP-STAT-KON-DX02437-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP STAT-KON DX02437 is a compound based on Polycarbonate resin containing conductive carbon powder, with good impact-resistance, flow and ESD performance, suitable for semi-con industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 16.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | Internal Method | ||
| Flow | 0.64 | % | |
| Across Flow | 0.68 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2570 | MPa | ASTM D638 |
| -- | 2550 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 58.0 | MPa | ASTM D638 |
| Yield | 58.0 | MPa | ISO 527-2/5 |
| Break 4 | 47.0 | MPa | ASTM D638 |
| Break | 47.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 5 | 19 | % | ASTM D638 |
| Break | 17 | % | ISO 527-2/5 |
| Flexural Modulus 6 | 2550 | MPa | ISO 178 |
| Flexural Stress 7 | ISO 178 | ||
| -- 8 | 92.0 | MPa | |
| -- 9 | 90.0 | MPa | |
| Flexural Strain at Break 10 | 7.8 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 11(23°C) | 26 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 12(23°C) | 95 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 0°C | 290 | J/m | ASTM D256 |
| 23°C | 360 | J/m | ASTM D256 |
| 0°C 13 | 20 | kJ/m² | ISO 180/1A |
| 23°C 14 | 25 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2100 | J/m | ASTM D4812 |
| 23°C 15 | 130 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 27.0 | J | ASTM D3763 |
| 23°C, Total Energy | 39.1 | J | ASTM D3763 |
| -- | 63.1 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 111 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 16 | 126 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 144 | °C | ISO 306/A50, ASTM D1525 17 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.8E+7 | ohms | ASTM D257 |
| Volume Resistivity | 1.4E+7 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 1.5 to 3.2 mm |
| 2 . | 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | Yield |
| 9 . | Break |
| 10 . | 2 mm/min |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*4 sp=62mm |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 mm |
| 17 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polypropylene LGF 7600 | Trinseo | PP, Unspecified | Polypropylene |
| Sasol Polymers PP CRV648 | Sasol Polymers | PP Impact Copolymer | Sasol Polymers PP |
| Moplen HP521J | LyondellBasell Industries | PP Homopolymer | Moplen |
| TRIMID® N66-100NL | Polymer Technology and Services, LLC | Nylon 66 | TRIMID® |
| Dynaprene® 1080A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |