HiFill FR® PC 1003 FR-NR UV
| Category: | PC , Polycarbonate |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill FR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vMs8rf_HiFill-FR-PC-1003-FR-NR-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill FR® PC 1003 FR-NR UV is a Polycarbonate (PC) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.14 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 57.9 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 430 | J/m | |
| 23°C, 3.18 mm | 640 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 132 | °C | |
| 1.8 MPa, Unannealed | 121 | °C | |
| CLTE - Flow | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 15 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 282 to 293 | °C | |
| Processing (Melt) Temp | 266 to 293 | °C | |
| Mold Temperature | 82.2 to 121 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 1009 | Chevron Phillips Chemical Company LLC | LDPE | Marlex® |
| ADDINYL B2 V15 | ADDIPLAST | Nylon 6 | ADDINYL |
| ANSABLEND A15 000 0000 T65 V0 | Daloga srl | PC+ABS | ANSABLEND |
| Braskem PP H7058-25R | Braskem Europe GmbH | PP Homopolymer | Braskem PP |
| POLIMAXX 1196NN | IRPC Public Company Limited | PP Homopolymer | POLIMAXX |