Jampilen HP422H
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Jam Polypropylene Company |
| Trademark: | Jampilen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uo89OF_Jampilen-HP422H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Jampilen HP422H is a modified homopolymer designed for the very high speed production of BOPP films, wherein an outstanding extrusion stability, thickness variation control, a very high drawability and readiness to a two way orientation would be achieved. The product contains a reinforced processing stabilization and features low water carry-over properties. Jampilen HP422H does not contain any slip or antistatic agent and is Calcium Stearate free. The Product is particularly suitable for metalizing film. BOPP films produced with Jampilen HP422H feature good mechanical properties, even at low temperatures, excellent barrier against moisture, odours, oils and oxygen and good transparency and gloss. Monolayer or coextruded films made of Jampilen HP422H with a thickness ranging from 20 to 40 µm are used for the packaging of foodstuffs, cosmetics and videocassettes. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.1 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 102 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 35.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 12 | % | ASTM D638 |
| Flexural Modulus | 1550 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 92.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 154 | °C | ASTM D1525 1 |
| Accelerated Oven Ageing (150°C) | 500 | hr | ASTM D3012 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (20.0 µm) | 0.50 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 GF 50 TSU | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Ateva® 1608 | Celanese EVA Performance Polymers | EVA | Ateva® |
| LEXAN™ SLX2571T resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| PLUSTEK PA301G2 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| LUVOCOM® 3-8437/EM/BL | LEHVOSS Group | Nylon 6 | LUVOCOM® |