PALSAFE®R 20 is a polycarbonate (PC) product,. It can be processed by injection molding and is available in Europe. PALSAFE®The application areas of R 20 include electrical/electronic applications and electrical appliances. Features include: flame retardant/rated flame high strength high hardness Impact resistance

General Information
Features	High strength Impact resistance, good Good liquidity High hardness
Uses	Electrical/Electronic Applications Electrical appliances
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.19	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg)	22.0	cm³/10min	ISO 1133
Water Absorption			ISO 62
Saturated, 23°C	0.30	%	ISO 62
Equilibrium, 23°C, 50% RH	0.18	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	2200	MPa	ISO 527-2/1A/1
Tensile Stress (Yield, 23°C)	61.0	MPa	ISO 527-2/1A/50
Tensile Strain (Yield, 23°C)	5.0	%	ISO 527-2/1A/50
Nominal Tensile Strain at Break (23°C)	50	%	ISO 527-2/1A/50

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	No Break		ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	143	°C	ISO 306/B50

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	275	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	V-2		UL 94

Additional Information
Melt-Volume Flow Rate, ISO 1133, 300°C/1.2 kg: 19 to 25 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2100 to 2300 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 59 to 63 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 4 to 6 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: >50 %Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 141 to 144 °CDensity, ISO 1183: 1.18 to 1.2 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.2 to 0.4 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 %

Additional Information

Melt-Volume Flow Rate, ISO 1133, 300°C/1.2 kg: 19 to 25 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2100 to 2300 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 59 to 63 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 4 to 6 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: >50 %Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 141 to 144 °CDensity, ISO 1183: 1.18 to 1.2 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.2 to 0.4 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 %

Resin Grade	Manufacturer	Category	Trademark
SLOVASTER® B1 BT TS	Plastcom	PBT	SLOVASTER®
XANTAR® LDS 3710	Mitsubishi Engineering-Plastics Corp	PC+ABS	XANTAR® LDS
Nanjing Hongrui PA66 A1304	Nanjing Hongrui Engineering Plastics Co., Ltd.	Nylon 66	Nanjing Hongrui PA66
Compoceran E102	Arakawa Chemical Industries, Ltd.	Epoxy	Compoceran
Kafrit PEX TA 2411 CL	Kafrit NA Ltd.	XLPE	Kafrit PEX

Category:	PC , Polycarbonate
Manufacturer:	pal plast GmbH
Trademark:	PALSAFE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	uh5iVM_PALSAFE-R-20.pdf
PRICE:	Order Products email sales@su-jiao.com