Marlex® HXM 50100-01

Category:	HDPE, HMW , High Density (HMW) Polyethylene
Manufacturer:	Chevron Phillips Chemical Company LLC
Trademark:	Marlex®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ufVXC6_Marlex-HXM-50100-01.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Marlex® HXM 50100-01 is a High Density (HMW) Polyethylene material. It is available in Latin America or North America for blow molding, extrusion, or thermoforming.

Important attributes of Marlex® HXM 50100-01 are:

Eco-Friendly/Green

Food Contact Acceptable

Hexene Comonomer

High ESCR (Stress Crack Resistant)

High Molecular Weight

Typical applications include:

Tanks

Automotive

Bags/Liners

Containers

Engineering/Industrial Parts

General Information
Features	Durable Food Contact Acceptable Good Melt Strength Hexene Comonomer High ESCR (Stress Crack Resist.) Low Temperature Impact Resistance Medium Rigidity Recyclable Material Ultra High Molecular Weight
Uses	Agricultural Tanks Automotive Applications Fuel Tanks Liners Pallets Shipping Containers
Agency Ratings	ASTM D 4976-PE235 FDA 21 CFR 177.1520(c) 3.2a
Forms	Pellets
Processing Method	Blow Molding Extrusion Thermoforming

Physical	Nominal Value	Unit	Test Method
Density	0.948	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/21.6 kg)	12	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance (100% Igepal, Compression Molded, F50)	> 600	hr	ASTM D1693B

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, Compression Molded)	66		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield, Compression Molded)	25.0	MPa	ASTM D638
Tensile Elongation ²(Break, Compression Molded)	750	%	ASTM D638
Flexural Modulus - Tangent ³(Compression Molded)	1200	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Tensile Impact Strength ⁴(Compression Molded)	170	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded)	69.0	°C	ASTM D648
Brittleness Temperature	< -75.0	°C	ASTM D746A
Vicat Softening Temperature	124	°C	ASTM D1525 ⁵

Note Message
1 .	Type IV, 51 mm/min
2 .	Type IV, 51 mm/min
3 .	13 mm/min
4 .	Type S
5 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
Mirakutoran® TPU F595FCOO	Japan Mirakutoran Inc.	TPU Alloy	Mirakutoran® TPU
BESTNYL SE15VI02AU	Triesa Plastics	Nylon 66	BESTNYL
EXCELLOY SX220	Techno Polymer Co, Ltd.	ABS	EXCELLOY
DynaStat® 147	Polymer Dynamix	TPO	DynaStat®
ENFLEX V1090A	ENPLAST Americas, a Ravago Group Company	TPV	ENFLEX