LNP™ STAT-LOY™ M3000C compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ubmG2i_LNP-STAT-LOY-M3000C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-LOY M3000C is a compound based on unfilled Polypropylene resin. Added features of this grade include: Clean Compound System, Antistat. Also known as: LNP* STAT-LOY* Compound M- CCS Product reorder name: M3000C |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.930 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 2.0 | % | |
| Across Flow : 24 hr | 1.0 to 2.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.16 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.16 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 769 | MPa | ASTM D638 |
| -- | 1180 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 18.0 | MPa | ASTM D638 |
| Break | 24.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 690 | % | ASTM D638 |
| Break | 690 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 862 | MPa | ASTM D790 |
| -- 5 | 1970 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 38.0 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 24.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 75 | J/m | ASTM D256 |
| 23°C 7 | 6.9 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 29.0 | J | ASTM D3763 |
| -- | 25.4 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 74.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 8 | 75.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 49.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 49.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.3E-4 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.3E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 to 1.0E+12 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 182 to 193 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 199 to 210 | °C | |
| Processing (Melt) Temp | 188 to 199 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203.3F | RTP Company | Nylon 12 | RTP |
| Sylvin 9917-89 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VINIKA® D6228 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | VINIKA® |
| LightSpan® LS-3443 | NuSil Technology | Silicone | LightSpan® |
| LNP™ THERMOCOMP™ OC006 compound | SABIC Innovative Plastics | PPS, Linear | LNP™ THERMOCOMP™ |