LNP™ LUBRICOMP™ KL004L compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IpVkNm_LNP-LUBRICOMP-KL004L-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP KL004L is a compound based on Acetal Copolymer resin containing 20% PTFE. Added features of this material include: Wear Resistant, Low Extractible. Also known as: LNP* LUBRICOMP* Compound FULTON 404 LE Product reorder name: KL004L |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.52 | g/cm³ | ASTM D792 |
| -- | 1.51 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 2.0 to 2.5 | % | |
| Across Flow : 24 hr | 2.0 to 2.5 | % | |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2760 | MPa | ASTM D638 |
| -- | 2340 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 47.6 | MPa | ASTM D638 |
| Yield | 48.0 | MPa | ISO 527-2 |
| Break | 46.9 | MPa | ASTM D638 |
| Break | 47.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 11 | % | ASTM D638, ISO 527-2 |
| Break | 22 | % | ASTM D638 |
| Break | 20 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2070 | MPa | ASTM D790 |
| -- | 2100 | MPa | ISO 178 |
| Flexural Stress | 59.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.25 | ||
| vs. Itself - Static | 0.14 | ||
| Wear Factor - Washer | 10.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 2 | 5.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 670 | J/m | ASTM D4812 |
| 23°C 3 | 39 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 4.70 | J | ASTM D3763 |
| -- | 1.40 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 154 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 146 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 84.4 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 83.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.2E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.2E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANAMID 66 A13^ F30 | Polykemi AB | Nylon 66 | SCANAMID 66 |
| BESTNYL SE00VI02AN | Triesa Plastics | Nylon 66 | BESTNYL |
| Hanwha Total PP RB210 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| OTECH ALLOY OTO9141LSZH - Riser Jacket | OTECH Corporation | TP, Unspecified | OTECH ALLOY |
| SIBUR Synthetic Rubber SBR-1706 Grade A | SIBUR | SBR, Emulsion | SIBUR Synthetic Rubber |