Spartech SC5-12B40 is a high viscosity, chemically coupled, PP homopolymer resin for injection molding that features 40% glass fiber reinforcement. It is heat stabilized and lubricated for good processing characteristics.

Polypropylene is a versatile thermoplastic offering a useful balance of heat and chemical resistance, good mechanical and electrical properties and processing ease. PP is resistant to deformation at elevated temperatures, it has good clarity and is resistant to impact at low temperatures.

A very versatile product for a wide variety of applications, Spartech SC5-12B40 is recommended for industrial, transportation, sporting goods and electrical/electronic applications.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 40% filler by weight
Additive	heat stabilizer Lubricant
Features	Chemical coupling Homopolymer Workability, good Good electrical performance Low temperature impact resistance Good chemical resistance Heat resistance, high Definition, high Thermal Stability Thermal stability, good Lubrication Viscosity, High
Uses	Electrical/Electronic Applications Industrial application Application in Automobile Field Sporting goods
Appearance	Available colors Natural color
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.20	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR)	5.0	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (23°C)	81.0	MPa	ASTM D638
Flexural Modulus (23°C)	6030	MPa	ASTM D790
Flexural Strength (23°C)	114	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	91	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	160	°C	ASTM D648

Injection	Nominal Value	Unit
Drying Temperature	90.6	°C
Drying Time	1.0	hr
Rear Temperature	216 - 227	°C
Middle Temperature	221 - 232	°C
Front Temperature	227 - 238	°C
Nozzle Temperature	232 - 243	°C
Processing (Melt) Temp	204 - 260	°C
Mold Temperature	26.7 - 37.8	°C

Resin Grade	Manufacturer	Category	Trademark
RTP PA6 L BLK	RTP Company	Nylon 6	RTP
Tekulac ST 40	TEKUMA Kunststoff GmbH	ABS	Tekulac
Moplen HP652P	LyondellBasell Industries	PP Homopolymer	Moplen
XANTAR® C CM 206 U	Mitsubishi Engineering-Plastics Corp	PC+ABS	XANTAR® C
ACCUCOMP™ ABS801V	ACLO Compounders Inc.	ABS	ACCUCOMP™