Optix® CA-927 G
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Plaskolite West, Inc. |
| Trademark: | Optix® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uPGf4E_Optix-CA-927-G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Optix® CA-927 G is a Polymethyl Methacrylate Acrylic product. It can be processed by injection molding and is available in North America. Typical application: Medical/Healthcare. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 4.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 55 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 50.2 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 5.3 | % | ASTM D638 |
| Flexural Modulus | 2140 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 75.8 | MPa | ASTM D790 |
| Compressive Strength | 72.4 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256 |
| Gardner Impact | 3.28 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 78.9 | °C | ASTM D648 |
| Vicat Softening Temperature | 112 | °C | ASTM D1525 |
| RTI Elec (1.50 mm) | 50.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 50.0 | °C | UL 746 |
| RTI Str (1.50 mm) | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 15 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 3.16 | ||
| 1 MHz | 2.52 | ||
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 0.040 | ||
| 1 MHz | 0.032 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 | |
| Transmittance | 91.3 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 182 to 238 | °C | |
| Middle Temperature | 199 to 254 | °C | |
| Front Temperature | 210 to 266 | °C | |
| Nozzle Temperature | 199 to 254 | °C | |
| Processing (Melt) Temp | 221 to 254 | °C | |
| Mold Temperature | 37.8 to 82.2 | °C | |
| Injection Pressure | 68.9 to 138 | MPa | |
| Back Pressure | 0.345 to 1.03 | MPa | |
| Screw Speed | 50 to 100 | rpm | |
| Clamp Tonnage | 14 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2000 B-430 | RTP Company | PSU Alloy | RTP |
| RTP 1000 GB 20 TFE 10 | RTP Company | PBT | RTP |
| SCLAIR® 2908C | NOVA Chemicals | HDPE | SCLAIR® |
| Elastollan® C 70 A 10 P 000 | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Moplen HP5035 | LyondellBasell Industries | PP Homopolymer | Moplen |