NORYL PPX™ PPX640F resin
| Category: | PPE+PS+PP , Polyphenylene Ether + PS + PP |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL PPX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uLCGG7_NORYL-PPX-PPX640F-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
40% GR PPE+PP. High elongation. high stiffness. NSF Standard 61 Compliant (color limited). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 1.3 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.17 to 0.18 | % | |
| Across Flow : 3.20 mm | 0.27 to 0.61 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 95.8 | MPa | |
| Break | 95.8 | MPa | |
| Tensile Elongation 2(Break) | 6.4 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 8320 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 50.0 mm Span) | 151 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 96 | J/m | |
| 23°C | 110 | J/m | |
| Unnotched Izod Impact (23°C) | 580 | J/m | ASTM D4812 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 14.1 | J | |
| 23°C, Total Energy | 16.8 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 159 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 146 | °C | |
| Vicat Softening Temperature | 163 | °C | ASTM D1525 5 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 1.1E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 to 76.7 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 243 to 288 | °C | |
| Middle Temperature | 249 to 288 | °C | |
| Front Temperature | 254 to 299 | °C | |
| Nozzle Temperature | 260 to 304 | °C | |
| Processing (Melt) Temp | 260 to 304 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.051 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Filter-bond™ E-3264 | Hapco Inc. | TS, Unspecified | Filter-bond™ |
| Hapflex™ 666 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| LNP™ STAT-LOY™ NX03583 compound | SABIC Innovative Plastics | PC+ABS | LNP™ STAT-LOY™ |
| Sylvin 802-90 UV CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 7833-95 Pink 6289 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |