LINATHENE® LL110
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | USI Corporation |
| Trademark: | LINATHENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yL5cnV_LINATHENE-LL110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LINATHENE LL110 is a linear low density polyethylene (LLDPE) developed for blown-film extrusion. Films made from LINATHENE LL110 have excellent impact strength, puncture strength, tear strength, tensile strength, elongation. LINATHENE LL110 is recommended for the manufacture of heavy duty bags, liner film and frozen food bags etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 9.81 | MPa | |
| TD : Yield | 8.83 | MPa | |
| MD : Break | 21.6 | MPa | |
| TD : Break | 15.7 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 500 | % | |
| TD : Break | 600 | % | |
| Dart Drop Impact 1 | 150 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 102 | °C | ASTM D1525 |
| Peak Melting Temperature | 122 | °C | ASTM D3418 |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU P495 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| SIBUR Synthetic Rubber NBR 4045 | SIBUR, LLC | NBR | SIBUR Synthetic Rubber |
| Sypex S1620GB | Ginar Technology Co., LTD. | SAN | Sypex |
| Diamond ASA S225 LG | Network Polymers, Inc. | ASA | Diamond ASA |
| Hifax TYC 852X E BLACK | LyondellBasell Industries | PP Copolymer | Hifax |