SUMIKASUPER® LCP E6406
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Sumitomo Chemical Co., Ltd. |
| Trademark: | SUMIKASUPER® LCP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u8ps7m_SUMIKASUPER-LCP-E6406.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKASUPER LCP is a thermotropic liquid crystalline polyester, showing the highest heat resistance among engineering plastics. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.030 | % | ASTM D955 |
| Transverse flow | 0.51 | % | ASTM D955 |
| Water Absorption (Saturation) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 151 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 17800 | MPa | ASTM D790 |
| Flexural Strength | 162 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | 330 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 287 | °C | ASTM D648 |
| Additional Information |
|---|
| Mold Shrinkage, Sumitomo Chemical Method, Machine Direction: 0.3 mils/inMold Shrinkage, Sumitomo Chemical Method, Transverse Direction: 5.1 mils/in |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Regrind | 30 | % | |
| Rear Temperature | 300 - 320 | °C | |
| Middle Temperature | 320 - 350 | °C | |
| Front Temperature | 340 - 370 | °C | |
| Nozzle Temperature | 340 - 370 | °C | |
| Mold Temperature | 70.0 - 160 | °C | |
| Injection Pressure | 78.0 - 157 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 20.0 - 39.0 | MPa | |
| Back Pressure | 0.980 - 4.90 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ferro PP TPP20AJ39UL GRAY | Ferro Corporation | PP Homopolymer | Ferro PP |
| Hypro® PP-CP 10/10 | Entec Polymers | PP Impact Copolymer | Hypro® |
| Perlast® G75TX | Precision Polymer Engineering Ltd. | Perfluoroelastomer | Perlast® |
| MARPOL® LL4F 801-B | Marco Polo International, Inc. | LLDPE | MARPOL® |
| ALTECH® ABS FC 1000/106 BK1280-05 | ALBIS PLASTIC GmbH | ABS | ALTECH® ABS |