LNP™ LUBRICOMP™ YL003 compound
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u32rTB_LNP-LUBRICOMP-YL003-compound-41106.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP YL003 is a compound based on Polyester Elastomer containing PTFE. Added features include; Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound YL-4030 Product reorder name: YL003 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow | 2.3 | % | Internal Method |
| Across Flow : 24 hr | 1.5 to 2.5 | % | ISO 294-4 |
| Flow : 24 hr | 1.5 to 2.5 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 180 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 24.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 460 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 230 | MPa | ISO 178 |
| Flexural Stress | 12.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 21 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | No Break | ISO 180/1U |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 182 to 193 | °C | |
| Middle Temperature | 204 to 216 | °C | |
| Front Temperature | 227 to 238 | °C | |
| Processing (Melt) Temp | 216 to 238 | °C | |
| Mold Temperature | 26.7 to 54.4 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000 GS 15 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| ACCUCOMP™ SAN900L | ACLO Compounders Inc. | SAN | ACCUCOMP™ |
| Geon™ Vinyl Flexible XV3861 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Hyundai EP PA66 LD150 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| Lupox® LW5402A | LG Chem Ltd. | PC+PBT | Lupox® |