RTP 1399 X 115071 D
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9sdkAg_RTP-1399-X-115071-D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber - Carbon Nanotube - ESD Protection |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.30 | % | ASTM D955 |
| Moisture Content | 0.040 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay | < 2.0 | sec | FTMS 101C 4046.1 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13800 | MPa | ASTM D638 |
| Tensile Strength | 117 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 0.80 | % | ASTM D638 |
| Flexural Modulus | 12400 | MPa | ASTM D790 |
| Flexural Strength | 186 | MPa | ASTM D790 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+3 to 1.0E+4 | ohms | ASTM D257 |
| -- | 1.0E+2 to 1.0E+3 | ohms | ESD STM11.11 |
| Volume Resistivity | < 1.0E+2 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Processing (Melt) Temp | 307 to 329 | °C | |
| Mold Temperature | 135 to 177 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 AR 15 TFE 15 | RTP Company | Nylon 66 | RTP |
| VITAMIDE® BB1XNT6253 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| INNOPOL® PP CS 1-2820 MA | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |
| Lumid® HI5001AS | LG Chem Ltd. | Nylon+Olefin | Lumid® |
| Lustran® ABS 288 | Styrolution | ABS | Lustran® ABS |