Niretan B 27 N
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niretan B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | toqonM_Niretan-B-27-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 coloured in bulk, high flow, for injection moulding, with short cycles and easy demoulding |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.14 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.80 - 2.0 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 9.0 | 10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | 80 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength 1(Yield) | 80.0 | 45.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 50 | 100 | % | ASTM D638 |
| Flexural Modulus 3 | 2900 | 90.0 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 110 | 40.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -20°C, 3.20 mm | 40 | 200 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 45 | 400 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 60.0 | -- | °C | ASTM D648 |
| Peak Crystallization Temperature (DSC) | 220 | -- | °C | ASTM D3418 |
| CLTE - Flow | 1.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 30 | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.50 | 4.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.10 | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | V-2 | -- | UL 94 | |
| 3.20 mm | V-2 | -- | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | -- | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 调节后的 Tensile Elongation @ Break, ASTM D638, 50 mm/min: >100%Notched Izod Impact, ASTM D256, 23°C, 3.2 mm: >400 J/mNotched Izod Impact, ASTM D256, -20°C, 3.2 mm: >200 J/m |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE B4520 | SABIC Americas, Inc. | HDPE | SABIC® HDPE |
| Xuchuan A-9001/B-8001D | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| KEBAFLEX® SG 60 A.01 | BARLOG plastics GmbH | TES | KEBAFLEX® |
| POTICON OB30 | Otsuka Chemical Co., Ltd. | PBT | POTICON |
| SQUARE® LIM3906-70A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |