PLUSTEK PA340S05
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | PLUSTEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rW2BVs_PLUSTEK-PA340S05.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 5% GLASS-BEADS REINFORCED POLYAMIDE 6.6, HEAT STABILIZED FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 1.4 to 1.8 | % | ASTM D955 |
| -- | 1.4 to 1.8 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 7.0 | % | ASTM D570 |
| Saturation, 23°C | 7.0 | % | ISO 62 |
| Equilibrium | 3.5 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 3.5 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 80.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 to 5.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 3100 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 135 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 50 | J/m | ASTM D256 |
| -- | 4.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 210 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 100 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 258 | °C | ISO 11357-3, ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.60 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V934 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SEPAZ™ LUB4343 | Mando Advanced Materials Co., Ltd. | PPS | SEPAZ™ |
| TRIREX® Compound VB3025G10 | Samyang Corporation | PC | TRIREX® Compound |
| Geon™ Vinyl Rigid Molding M4820 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |
| EPAMOULD 260A56 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |