Generic ECTFE
| Category: | ECTFE , Ethylene Chlorotrifluoroethylene Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tilexZ_Generic-ECTFE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic ECTFE This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 1.0 to 25 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 90 | ASTM D785 | |
| Durometer Hardness (23°C) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1650 to 1660 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 29.6 to 30.1 | MPa | |
| Break, 23°C | 46.5 to 54.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 5.0 to 9.9 | % | |
| Break, 23°C | 240 to 250 | % | |
| Flexural Modulus (23°C) | 1690 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 47.0 | MPa | ASTM D790 |
| Coefficient of Friction | 0.20 | ASTM D1894 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 90.0 to 90.6 | °C | |
| 1.8 MPa, Unannealed | 64.9 to 65.2 | °C | |
| Brittleness Temperature | -76.1 to -73.7 | °C | ASTM D746 |
| Melting Temperature | 225 to 242 | °C | |
| Peak Crystallization Temperature (DSC) | 222 to 223 | °C | ASTM D3418 |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 5.4E+16 to 5.5E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 14 to 19 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 2.57 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 52 | % | ASTM D2863 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Medalist® MD-50278 | Teknor Apex Company | TPE | Medalist® |
| Multi-Flex® TPE A8030 | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| KRATON® G4609 H | Kraton Polymers LLC | SEBS | KRATON® |
| LEXAN™ SLX1431D resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Petrothene® LR734011 | LyondellBasell Industries | HDPE | Petrothene® |