SLOVALEN® PH 49 GF 60
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Plastcom |
| Trademark: | SLOVALEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wpoldq_SLOVALEN-PH-49-GF-60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Modified homopolymer PP for injection moulding, chemically reinforced with 60% glass fibre, contains the modifier of mechanical properties.Very good strength and tensile modulus. Delivered in natural mode and in the full RAL colour scale. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 0.38 | % | |
| Flow | 0.43 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12800 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 125 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 10100 | MPa | ISO 178 |
| Flexural Stress | 160 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 9.0 | kJ/m² | |
| 23°C | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 45 | kJ/m² | |
| 23°C | 45 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 175 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 182 | °C | ISO 306/B |
| Melting Temperature (DSC) | 160 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Pressure | 100 to 140 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultradur® B 4300 G2 BK5110 | BASF Corporation | PBT | Ultradur® |
| Nypol® PA B3 HL AML0308 NT359 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Chiao Fu PA6 MC212G30 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 6 | Chiao Fu PA6 |
| FRAGOM PR/412 | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| PALMID® R 12 E | pal plast GmbH | Nylon 12 | PALMID® |