TECHNYL® C 52G1 V20 GREY R7035 CF
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | td4fqB_TECHNYL-C-52G1-V20-GREY-R7035-CF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Halogen and Red Phosphorous free fire resistant polyamide PA6 Glass reinforced for injection moulding of thin walled parts |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.90 | -- | % | |
| Water Absorption (23°C, 24 hr) | 1.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 6700 | 4550 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 92.0 | 65.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 2.9 | 4.8 | % | ISO 527-2/1A |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -- | 3.2 | 8.6 | kJ/m² | |
| -30°C | 3.1 | 3.4 | kJ/m² | |
| Charpy Unnotched Impact Strength | 39 | 79 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 170 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Electric Strength | 31 | 27 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | V-2 | -- | ||
| 1.60 mm | V-2 | -- | ||
| 3.20 mm | V-2 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 960 | -- | °C | |
| 1.60 mm | 960 | -- | °C | |
| 3.20 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.800 mm | 725 | -- | °C | |
| 1.60 mm | 700 | -- | °C | |
| Oxygen Index | 29 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 245 to 255 | °C | |
| Mold Temperature | 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 TFE 15 SI Z | RTP Company | PC | RTP |
| RTP EMI 260.5 H | RTP Company | Nylon 66 | RTP |
| Terblend® N NM-19XP | INEOS Styrolution Group GmbH | ABS+Nylon | Terblend® N |
| NILENE® E10 K40T | Taro Plast S.p.A. | PP Copolymer | NILENE® |
| DURACON® CH-10 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |