Reny® 1521AH
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rxHH26_Reny-1521AH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Reny® 1521AH is a Polyarylamide (PARA) material filled with 50% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Reny® 1521AH are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.73 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.47 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.13 | % | |
| Equilibrium, 23°C, 50% RH | 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 20600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 215 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 18900 | MPa | ISO 178 |
| Flexural Stress | 339 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 49 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 238 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 228 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength | IEC 60243-1 | ||
| 2.00 mm | 20 | kV/mm | |
| 3.00 mm | 17 | kV/mm | |
| Comparative Tracking Index | 350 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 265 | °C | |
| Front Temperature | 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Mold Temperature | 120 to 145 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTFA 12 | Polymer Tailoring Ltd. | PP, Unspecified | PTFA |
| Sinvicomp STG8501 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Spartech Polycom PP5420 | Spartech Polycom | PP, Unspecified | Spartech |
| DOWLEX™ 2035G | The Dow Chemical Company | LLDPE | DOWLEX™ |
| Sylvin 2970-60 Clear 8382 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |