Ensinger TECAPET®
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Ensinger Inc. |
| Trademark: | Ensinger |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tcbx54_Ensinger-TECAPET-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TECAPET®PET is an unreinforced, semicrystalline thermoplastic polyester derived from polyethylene terephthalate. Its excellent wear resistance, low coefficient of friction, high flexural modulus, and superior dimensional stability make it a versatile material for designing mechanical and electro-mechanical parts. Because TECAPET®PET has no centerline porosity, the possibility of fluid absorption and leakage is virtually eliminated. TECAPET™PET superior wear resistance and lack of centerline porosity give it an advantage over other materials for applications involving solvents, chemicals, and food products. TECAPET™PET is also used in water purification systems, printing equipment, textile components, food-handling equipment, and valves. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.10 | % | ASTM D570 |
| Saturated, 23°C | 0.50 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 23°C) | 94 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3240 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 86.2 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 20 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2960 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 121 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| With self-dynamics 1 | 0.25 | ASTM D1894 | |
| With Self-Static | 0.19 | ASTM D1894 | |
| Wear Factor 2(0.28 MPa, 0.25 m/sec) | 420 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 116 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 79.4 | °C | ASTM D648 |
| Peak Melting Temperature | 254 | °C | ASTM D3418 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1170 | J/kg/°C | |
| Maximum Service Temperature | |||
| Intermittent | 160 | °C | |
| Long Term | 110 | °C | UL 746B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 16 | kV/mm | ASTM D149 |
| Dielectric Constant 3(23°C, 60 Hz) | 3.40 | ASTM D150 | |
| Dissipation Factor (23°C, 60 Hz) | 2.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Data obtained from extruded shapes material. |
| Note Message | |
|---|---|
| 1 . | 40 psi, 50 fpm |
| 2 . | Against Steel |
| 3 . | 50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Boda BDF2602AP | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Fiberfil® J-60/40/E | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| EPO-TEK® TJ1183-LH | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Karina IVORY PVC COMPOUND -E 832-35/ 1-Y-ERA-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ COLORCOMP™ 310C compound | SABIC Innovative Plastics | PBT | LNP™ COLORCOMP™ |