PENTAMID B GK30 H schwarz
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tb4TMd_PENTAMID-B-GK30-H-schwarz.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, heat stabilised polyamide 6, 30% glass bead reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 0.80 | -- | % | ISO 294-4 |
| Flow direction | 0.80 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 6.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.1 | -- | % | ISO 62 |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 185 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 4300 | 2150 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 75.0 | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 8.0 | 25 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 195 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 80.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 222 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength (1.00 mm) | 30 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.90 | -- | IEC 60250 | |
| Comparative Tracking Index | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 ISO Description: PA6, MHRC, 14-040 N, GB30The value listed as Melting Point, ISO 3146, was tested in accordance with ISO 11357. |
| 调节后的 ISO Description: PA6, MHRC, 14-040 N, GB30Tensile Strain at Break, ISO 527: >25% |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.090 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 255 - 280 | °C | |
| Middle Temperature | 270 - 285 | °C | |
| Front Temperature | 270 - 280 | °C | |
| Processing (Melt) Temp | 275 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Pressure | 70.0 | MPa | |
| Holding Pressure | 42.0 | MPa | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| alphalon™ 25 | Grupa Azoty ATT Polymers GmbH | Nylon 6 | alphalon™ |
| BMC 404 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| FRblend® PC-1304 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC | FRblend® |
| Grilamid® XE 4181 nat | EMS-GRIVORY | Nylon 1010 | Grilamid® |
| POCAN® B 3233 HR 000000 | LANXESS GmbH | PBT | POCAN® |