Hanwha Total PE F120U
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tSM8vB_Hanwha-Total-PE-F120U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| F120U is a high-density polyethylene resin for films. This grade is designed to be processed in conventional blown film equipment. F120U is generally used for mulching films because of high UV stabilizer content in the additive formulation. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.956 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.044 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 55 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 22.6 | MPa | ASTM D638 |
| Fracture | 29.4 | MPa | ASTM D638 |
| Apparent Bending Modulus | 981 | MPa | ASTM D747 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 20 µm | 53.9 | MPa | ASTM D882 |
| TD : Break, 20 µm | 49.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 380 | % | ASTM D882 |
| TD : Break, 20 µm | 450 | % | ASTM D882 |
| Dart Drop Impact (20 µm) | 200 | g | ASTM D1709 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 290 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 124 | °C | ASTM D1525 1 |
| Additional Information |
|---|
| Elmendorf Tear Strength MD, ASTM D785: 6 kg force/cm²Elmendorf Tear Strength TD, ASTM D785: 200 kg force/cm² |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 - 190 | °C | |
| Cylinder Zone 2 Temp. | 160 - 190 | °C | |
| Cylinder Zone 3 Temp. | 160 - 190 | °C | |
| Cylinder Zone 4 Temp. | 160 - 190 | °C | |
| Cylinder Zone 5 Temp. | 160 - 190 | °C | |
| Die Temperature | 180 - 210 | °C |
| Extrusion instructions |
|---|
| Blow up ratio: 3 to 6Frost Line Height: 40 to 120 cm |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT2600-677UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| XANTAR® 18 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Nypol® PA A3 G25 FR NTLA010 NR443 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| KumhoSunny ABS 740 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| MAJORIS FTR212 - 8229 | AD majoris | PP, Unspecified | MAJORIS |