Infino TK-4046H
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tG3EwT_Infino-TK-4046H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino TK-4046H is a Polyphthalamide (PPA) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (330°C/5.0 kg) | 25 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 3.20 mm | 0.75 | % | |
| Across Flow : 3.20 mm | 0.86 | % | |
| Ash Content | |||
| -- | 41 | % | ASTM D5630 |
| -- | 41 | % | ISO 3451 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Initial Reflectance (440 nm) | 94 | % | ASTM E1331 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4800 | MPa | ASTM D638 |
| -- | 6200 | MPa | ISO 527-2/5 |
| Tensile Strength | |||
| Yield 2 | 110 | MPa | ASTM D638 |
| Yield | 100 | MPa | ISO 527-2/5 |
| Break 3 | 110 | MPa | ASTM D638 |
| Break | 100 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 4 | 2.4 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 7400 | MPa | ASTM D790 |
| -- 6 | 6300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 140 | MPa | ASTM D790 |
| -- 8 | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 24 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 35 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 33 | J/m | ASTM D256 |
| 23°C 10 | 4.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 4.00 mm | 265 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 240 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yellowness Index (3.20 mm) | 4.0 | YI | ASTM D1925 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Desiccant Dryer | 120 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 285 to 290 | °C | |
| Middle Temperature | 295 | °C | |
| Front Temperature | 295 to 300 | °C | |
| Nozzle Temperature | 300 | °C | |
| Mold Temperature | 130 to 160 | °C | |
| Injection Pressure | 118 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stylac™ IC10N | Asahi Kasei Chemicals Corporation | ABS | Stylac™ |
| ACCUTECH™ CP0437T10L1 | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| CLEARTUF AQUA D82 | M&G Gruppo Mossi & Ghisolfi | PET | CLEARTUF |
| Durez® 22257 (Compression) | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| LNP™ LUBRICOMP™ EFL36 compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |