Ultrason® S 3010 MR UN
| Category: | PSU , Polysulfone |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultrason® S |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tDYnUa_Ultrason-S-3010-MR-UN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced, higher viscosity injection moulding and extrusion grade, tougher, with improved chemical resistance and demolding optimized. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 to 0.80 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (360°C/10.0 kg) | 45.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.73 | % | |
| Flow | 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.80 | % | |
| Equilibrium, 23°C, 50% RH | 0.30 | % | |
| Viscosity Number | 72.0 | cm³/g | ISO 307 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 135 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 75.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.8 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 5.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 5.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 177 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 187 | °C | ISO 11357-2 |
| CLTE - Flow | |||
| 23 to 80°C | 5.3E-5 | cm/cm/°C | ISO 11359-2 |
| 140°C | 6.0E-5 | cm/cm/°C | DIN 53752 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.00 mm | V-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 330 | °C | |
| Middle Temperature | 340 | °C | |
| Front Temperature | 350 | °C | |
| Nozzle Temperature | 350 | °C | |
| Processing (Melt) Temp | 330 to 390 | °C | |
| Mold Temperature | 120 to 160 | °C | |
| Screw Speed | < 300 | mm/sec |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4600 EA 534 | RTP Company | SPS | RTP |
| Sanren Q200 (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | LDPE | Sanren |
| Bayflex® 956 | Covestro - PUR | PUR-MDI | Bayflex® |
| Andur AL 80-5 AP/Curene® 110 | Anderson Development Company | PUR-Eth,aliphat | Andur |
| Plaslube® PC GF10 TL4 | Techmer Engineered Solutions | PC | Plaslube® |