LNP™ THERMOCOMP™ QF00A compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tCTbSX_LNP-THERMOCOMP-QF00A-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP QF00A is a compound based on Nylon 6/10 containing 50% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound QF-100-10 Product reorder name: QF00A |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.18 to 0.20 | % | |
| Across Flow : 24 hr | 0.50 to 1.5 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.21 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.28 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 18700 | MPa | ASTM D638 |
| -- | 15500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 181 | MPa | ASTM D638 |
| Yield | 182 | MPa | ISO 527-2/5 |
| Break 3 | 181 | MPa | ASTM D638 |
| Break | 182 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.6 | % | ASTM D638 |
| Yield | 2.3 | % | ISO 527-2/5 |
| Break 5 | 2.6 | % | ASTM D638 |
| Break | 2.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 11400 | MPa | ASTM D790 |
| -- 7 | 12900 | MPa | ISO 178 |
| Flexural Strength 8 | ASTM D790 | ||
| Yield, 50.0 mm Span | 280 | MPa | |
| Break, 50.0 mm Span | 285 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 160 | J/m | ASTM D256 |
| 23°C 9 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1300 | J/m | ASTM D4812 |
| 23°C 10 | 75 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 221 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 220 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 213 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 206 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9446-79 Natural | Sylvin Technologies Incorporated | PVC+PUR | Sylvin |
| WEVO-CHEMIE Polyurethanes PU 7210 FL/507 | WEVO-CHEMIE GmbH | PUR, Unspecified | WEVO-CHEMIE Polyurethanes |
| NORYL™ 141E resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |
| E-FLEX™ S1060 | Mando Advanced Materials Co., Ltd. | TPE | E-FLEX™ |
| LEXAN™ HPS1R resin | SABIC Innovative Plastics | PC | LEXAN™ |