Hostacom X M2 T20 3 BLACK
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t8Sk7s_Hostacom-X-M2-T20-3-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| "Hostacom" X M2 T20 3 BLACK is a 16% mineral filled PP copolymer for injection molding. It combines good stiffness/impact balance. The grade is available in not specified BLACK color only. It is not intended for medical, pharmaceutical or drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 6.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 1500 | MPa | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 18.0 | MPa | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 30 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 95.0 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4165 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 200H TFE 10 SI 1 | RTP Company | Nylon 66 | RTP |
| Deprene 253-40 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |
| ESTOPLAST XU 5230BB11 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |
| TOPAS® 9506F-500 | Polyplastics Co., Ltd. | COC | TOPAS® |