MAXAMID™ PA66G50
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Pier One Polymers, Inc. |
| Trademark: | MAXAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ro7I2f_MAXAMID-PA66G50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MAXAMID™ PA66G50 is available in black and natural, internal and external lubricants, UV stabilized and other modifications. Further information and details are available upon request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.59 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 228 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 15900 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 297 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 252 | °C | ASTM D648 |
| Peak Melting Temperature | 256 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | < 0.20 | % | |
| Processing (Melt) Temp | 290 to 305 | °C | |
| Mold Temperature | 65.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2105 TFE 5 | RTP Company | PEI | RTP |
| Mold Max® XLS II | Smooth-On, Inc | Silicone | Mold Max® |
| ALTECH® PP-H A 2020/576 GF20 CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| Grilon® TSGZ-15 | EMS-GRIVORY | Nylon 66/6 | Grilon® |
| Karina WHITE COLOR CONCENTRATE 10/ 96-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |