Fibremod™ GE225U
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Fibremod™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t2WG9N_Fibremod-GE225U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fibremod GE225U is a 20% chemically coupled glass fibre reinforced polypropylene compound intended for injection moulding. This material shows excellent mechanical properties also at elevated temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | |||
| Vertical flow direction : 2.00mm | 1.0 | % | ISO 294-4 |
| Flow direction : 2.00mm | 0.20 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (1.00 mm) | 5000 | MPa | ISO 527-2 |
| Tensile Stress | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.9 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 4200 | MPa | ISO 178 |
| Flexural Stress | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 22 | kJ/m² | ISO 179/1eU |
| 23°C | 32 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 145 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 135 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 160 | °C | ISO 306/A |
| -- | 126 | °C | ISO 306/B |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | 35.0 | µgC/g | VDA 277 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperature: 40 - 80°CMass Temerature: 220 - 260°CBack Pressure: As low as possibleScrew Speed: Low to MediumFlow Front Speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 150x80x2 |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NILFLEX® SH A70 MC009 | Taro Plast S.p.A. | SEBS | NILFLEX® |
| Baoding 68T80 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| Hostacom G3 N01 102297 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Lucent ABS ABS-305LG | Lucent Polymers, Inc. | ABS | Lucent ABS |
| Paracril® P7092P | INSA | NBR | Paracril® |